Polyvinyl Chloride (PVC or Vinyl) is a high strength thermoplastic material widely used in applications, such as pipes, medical devices, wire and cable insulation...the list is endless. It is the world's third-most widely produced synthetic plastic polymer.
Polyvinyl Chloride can be injection moulded just like other plastics but the inclusion of chlorine in the material complicates the process. This is because melted PVC can give off a corrosive toxic gas. Accordingly, shops need to be equipped with sufficient ventilation systems. Those that aren’t are likely to be hesitant to work with the material. Additionally, special corrosive resistant materials like stainless steel or a chrome plating are required for the mould tool during PVC plastic injection moulding. Shrinkage in PVC tends to be between one and two percent but can vary based on a number of factors including material durometer (hardness), gate size, holding pressure, holding time, melt temperature, mould wall thickness, mould temperature, and the percentage and type of additives.
General performance PVC resin is a white or light yellow powder with a relative density of 1.35-1.45. The hardness of the product can be added by PVC transparent board PVC transparent board. Adjust the number of plasticizers. Pure PVC has low water absorption and permeability.
Thermal properties: The thermal stability of PVC is very poor. It begins to decompose at 140 ° C and the melting temperature is 160 ° C. The coefficient of linear expansion of PVC is small, and it is flame retardant, and the oxidation index is as high as 45 or more.
Electrical properties: PVC is a polymer with better electrical properties, but due to its greater polarity, electrical insulation is not as good as PP and PE. Dielectric constant, dielectric loss tangent and volume resistivity are large, corona resistance is not good, generally suitable for low-voltage and low-frequency insulating materials.
PVC can adopt injection moulding, extrusion, blow moulding, calendering, plastic lining, foaming and other moulding processes. For plasticized PVC products, plasticizer and other additives shall be added to PVC powder or granular materials for premixing and plasticization before moulding. When the plasticized plastic is suitable for processing, such as injection moulding and basic processes, basic granulation is required. When used in the calendering process, it needs to be pressed into a soft plate before. Injection moulding is mainly used for UPVC.
PVC melting temperature during processing is a very important process parameter, if pvc moulding temperature is not appropriate will lead to the problem of material decomposition.
PVC has poor stability to light and heat. What is the pvc plastic melting point? PVC injection begins to soften at 65-85 °C, above 170C into a viscous flow state, 140 °C begins to decompose a small amount, with the increase of temperature decomposition rate increases, above 190°C a large amount of HCL gas is released. PVC has a chlorine content of up to 56%, so it is flame retardant and self-extinguishing. PVC has good dielectric properties and is an excellent electrical insulation material. In addition, PVC plastic injection moulding is a polymer with poor thermal stability, which can gradually liberate HCl under the action of light and heat, and at the same time, in the presence of forces, oxygen, ozone, cyanide chloride and some active metal (such as copper, zinc, etc.) ions, the degradation rate is greatly accelerated.